High Temperature Resistant Sculpt Ultra White TDS
1. Product Introduction
Siraya Tech Simple resin offers easy cleaning with water or 15% alcohol.
Its low viscosity and minimal peel force enable high-speed printing on large 16K printers. This low-odor formula prevents yellowing, while Simple Clear restores to full transparency with easier post-processing, making it an ideal choice for beginners.
Application:
- Low-run injection molds
- Vacuum forming
- Dental Application
- Artistic sculptures
- Designed for vulcanized rubber process
Check out Sculpt Ultra White Resin here
2. Property Data
|
Mechanical Properties |
Measure |
Method |
|
Tensile Stress at Yield |
33 |
ASTM D638 |
|
Tensile Stress at Break |
31 |
ASTM D638 |
|
Young’s Modulus |
8000 |
ASTM D638 |
|
Elongation at Break |
1 |
ASTM D638 |
|
Flexural Modulus |
7500 |
ASTM D790 |
|
Flexural Stress at Yield |
120 |
ASTM D790 |
|
Flexural Strain at Break |
14 |
ASTM D790 |
|
Other Properties |
Measure |
Method |
|
HDT at 0.455 MPa |
250 |
ASTM D648 |
|
IZOD Impact (Notched) J |
22 |
ASTM D256 |
|
Shore Hardness |
99D |
ASTM D2240 |
|
Solid Density |
1.6 |
ASTM 792 |
|
Water Absorption (24hr) |
0.01% |
ASTM D570 |
|
Liquid Properties |
Measure |
Method |
|
Viscosity at 25°C (77°F) |
650 |
ASTM D7867 |
|
Liquid Density |
1.22 |
ASTM D1475 |
3. Work Flow
Before Printing
|
Steps |
Key Point |
|
1 |
Before opening the bottle for the first time, warm up the bottle, turn it over for 25℃, then shake it up and down for 1-2 minutes. |
|
2 |
Please keep the print temperature at 25-30 °C. |
|
3 |
Before printing Sculpt Ultra, shake it up and down for 1-2 minutes. |
|
4 |
Use a plastic scraper to mix up the resin already in the vat. |
Printing
|
Material Name |
Sculpt High-Temp Resin (Ultra White) |
|
Primary Printer Compatibility |
MSLA / LCD/ DLP 3D Printers |
|
Secondary Printer Compatibility |
385nm - 405nm 3D Printers |
|
Hardware Requirement |
Access to exposure control is required |
|
Supported Slicer Software |
Chitubox, Lychee Slicer, Anycubic Photon Workshop, Blueprint Studio, Elegoo Satellite |
|
Slicer Profiles Download |
Cleaning
|
Cleaning Step / Category |
Instructions & Recommendations |
|
Cleaning Solvents |
• Preferred: 95% concentrated Ethanol or IPA. • Alternative: Methanol (must not contain acetone) |
|
Cleaning Time |
Submerge parts in the solvents several times for a total of 4-5 minutes, using the ultrasonic cleaner. |
|
Submersion Limit |
Do not submerge parts in alcohol for more than 5 minutes. |
|
Extra Step |
For a complex model, use a painter brush (or any brush made with hair) to gently remove excess resin from the printed part. |
Drying
|
Drying |
Remove alcohol by using an oven for 7-8 minutes (using a hair dryer requires 10 minutes) |
|
Note: For complex parts with cavities, repeat the clean/dry cycle multiple times. |
|
|
Quality Check |
Touch the dried surface. If it is still sticky, wash and dry the part again until smooth. |
Post-Curing
|
Step / Factor |
Instructions & Recommendations |
|
Preparation |
Ensure the resin is completely cleaned off and absolutely no alcohol is left on the print before curing. |
|
UV Specifications |
Use a UV light source with a wavelength of 395-405nm. |
|
Curing Time |
Cure for approximately 15 minutes to reach optimal strength. Parts must be fully cured before use. |
|
Recommended Method |
Direct curing without water for moisture control. |
Sanding
|
Preparation |
1000 grit sandpaper and mineral oil or water |
|
Tips |
Mineral oil adds luster |
Mold Release Recommendation
|
1 |
|
|
2 |
|
|
Tips |
Our User has said that Rustoleum Clear Coat Engine Enamel worked well as a release coating. |
|
Explanation |
Sculpt Ultra is different from metal mold and the normal Sculpt Mold. 1. Sculpt Ultra is made with composite and has a rougher surface. 2. This rougher surface leads to a stronger grip on the injected material. 3. Mold releases and coating can fill in those tiny surface valleys so it has less grip to the parts. |
More information：
Check out Sculpt Ultra White User Guide