Blu Tough - Blu Lava Black TDS

This TDS is forĀ BluĀ Lava Black only.

1. Product Introduction

  • Exceptional Strength and Stiffness: Engineered for PC-like strength;
  • High-Resolution Prints: Provides precise, high-quality prints;
  • Excellent Impact Resistance and Tappability;
  • Biocompatibility: Certified under ISO 10993-5 / 10993-10.

Application:

  • Engineering Prototypes
  • End-Use Parts
  • Medical Device Prototypes
  • Parts that require both strength and precision

    2. Property Data

    Mechanical Properties (Unit) Measure Method
    Tensile Stress at Yield (Mpa) 65 ASTM D638
    Tensile Stress at Break (MPa) 60 ASTM D638
    Youngā€™s Modulus (MPa) 2500 ASTM D638
    Elongation at Break(%) 12 ASTM D638
    Flexural Modulus (Mpa) 2600 ASTM D790
    Flexural Stress at Yield (MPa) 65 ASTM D790
    Flexural Strain at Break(MPa) - ASTM D790
    Other Properties (Method) Measure
    HDT at 0.455 MPa 75
    IZOD Impact (Notched) J/m 47
    Shore Hardness (D) 87D
    Solid Density g/cm3 1.15
    Water Absorption (24hr) 2%
    Biocompatibility Yes 10993-10/5
    Liquid Properties Measure
    Viscosity CPS @ 25Ā°C (77Ā°F) 1600 25Ā°C (77Ā°F)
    Liquid Density g/mL 1.1

    Ā 

    3. Work Flow

    • Printing

    Blu Lava Black PC-like resin is a versatile material that can be used with different types of 3D printers. It is specially designed for MSLA/LCD printers yet, it can also be printed on some of the 405nm SLA and DLP printers if you have access to exposure control.

    To achieve optimal results with BluĀ Lava BlackĀ resin, you need to use the appropriate slicer profiles for your printer model and software. You can download the slicer profiles for Chitubox and Lychee slicers from this link: Profiles for DifferentĀ Printers

    Please download the test model and view the tutorial: V5 Test model.

    Ā 

    • Clean

    Due to Blu Lava Black's higher viscosity, thorough cleaning is crucial:

      • After printing, let the part drain thoroughly over the vat for at least 10 minutes.
      • Use an ultrasonic cleaner with 90% or higher concentrated Ethanol or IPA (Isopropyl Alcohol) to clean for 10 minutes.
      • After cleaning, use compressed air or a hair dryer on a cool setting to thoroughly dry the part.
      • Check the dried surface by touch - if it feels sticky, clean and dry again.

    Ā 

    • Post Curing
      • Ensure the part is completely clean and dry before post-curing.
      • Use a 395-405nm UV light source for curing.
      • Cure for approximately 15-20 minutes, rotating the part every 5 minutes for even
      • exposure.
      • For optimal results, submerge the part in water during curing to increase efficiency.

      4. Biocompatibility Certification

      ForĀ Biocompatibility-related applications, please follow the post-processing guideline here.

      5. Additional Information

      Download BluĀ LavaĀ BlackĀ TDS in PDF Version.