Blu Tough - Blu Nylon Black TDS
This TDS is for Blu Nylon Black only.
Check out Blu Nylon Black here.
1. Product Introduction
- Blu Nylon Black is a tough engineering resin that has excellent mechanical properties.
- High hardness and robustness make it suitable for various parts and tool making.
- It is also bio-compatible as certified under ISO 10993-10/5.
- Higher impact resistance than normal Blu.
Application:
- Engineering Prototypes
- Mechanical Aids
- Fixtures and Jigs
- Medical Devices
- Load-bearing parts
2. Property Data
| Mechanical Properties (Unit) | Measure | Method |
| Tensile Stress at Yield (Mpa) | 47 | ASTM D638 |
| Tensile Stress at Break (MPa) | 45 | ASTM D638 |
| Young’s Modulus (MPa) | 1750 | ASTM D638 |
| Elongation at Break(%) | 50 | ASTM D638 |
| Flexural Modulus (Mpa) | 1900 | ASTM D790 |
| Flexural Stress at Yield (MPa) | - | ASTM D790 |
| Flexural Strain at Break(MPa) | - | ASTM D790 |
| Other Properties (Method) | Measure | |
| HDT at 0.455 MPa | 63 | |
| IZOD Impact (Notched) J/m | 53 | |
| Shore Hardness (D) | 78D | |
| Solid Density g/cm3 | 1.15 | |
| Water Absorption (24hr) | 2% | |
| Biocompatibility | Yes | 10993-10/5 |
| Liquid Properties | Measure | |
| Viscosity CPS @ 25°C (77°F) | 750 | 25°C (77°F) |
| Liquid Density g/mL | 1.1 |
3. Work Flow
- Printing
Blu-tough resin is a versatile material that can be used with different types of 3D
printers. It is specially designed for MSLA/LCD printers yet, it can also be printed on some of the 405nm SLA and DLP printers if you have access to exposure control.
To achieve optimal results with Blu Nylon Black resin, you need to use the appropriate slicer profiles for your printer model and software. You can download the slicer profiles for Chitubox and Lychee slicers from this link: Profiles for Different Printers
Please download the test model and view the tutorial: V5 Test model.
- Clean
Here are some tips for cleaning your printed parts:
- Use a painter brush (or any brush made with hair) to remove excess resins on the printed part.
- Use 95% concentrated Ethanol (preferred) or IPA to clean. Some form of methanol should work but make sure it does not contain acetone.
- Do not submerge the parts in alcohol for more than 5 minutes.
- After cleaning, remove alcohol as soon as possible with a hair dryer or air blower.
- For complex parts with lots of cavities, it may be a good idea to clean/dry multiple times.
You can check by touching the dried surface of the part to see if it is still sticky. If
the dried surface is still sticky, wash some more and dry again.
- Post Curing
Here are some tips for post-curing your printed parts:
- Blu reached its optimal strength when the printed part was post-cured with UV light after cleaning. Use 395-405nm UV light and cure for about 15 minutes.
- Make sure the resin is completely cleaned off, and there is no alcohol left (it needs to be dry) on the print before curing.
- Curing by submerging the object in water will significantly increase curing efficiency.
4. Biocompatibility Certification
For Biocompatibility related applications, please follow the post-processing guideline here.
5. Additional Information
Download Blu Nylon Black TDS in PDF Version.
Come and View Blu Nylon Black User Guide